2004 年 45 巻 2 号 p. 193-198
Melt-spun, rapid solidified Fe-Ga ribbon sample exhibited large magnetostriction and good ductility as compared with conventional bulk sample. But the origin was not clear yet. In order to investigate the occurrence of large magnetostriction in Fe-Ga ribbon sample, the correlation between magnetostriction and the crystal grain morphology was inspected in detail by SEM/EBSP method for Fe-15 at%Ga alloy. In comparison with as-spun ribbon sample, short-time (0.5 h) heat treated ribbon had stronger [100] oriented texture and exhibited larger magnetostriction of 140 ppm (×10−6) at 800 kA/m. These phenomena suggest that such a large magnetostriction is caused by the release of considerable large internal stresses in as-spun ribbon as well as the remained strong textures after annealing.