Preparation of Calcium Phosphate Films by Radiofrequency Magnetron Sputtering
Takayuki NarushimaKyosuke UedaTakashi GotoHiroshi MasumotoTomoyuki KatsubeHiroshi KawamuraChiaki OuchiYasutaka Iguchi
Author information
JOURNAL FREE ACCESS

2005 Volume 46 Issue 10 Pages 2246-2252

Details
Abstract

Calcium phosphate films were prepared on titanium substrates by radiofrequency (RF) magnetron sputtering at RF powers from 75 to 150 W. Hot-pressed β-tricalcium phosphate (β-TCP) plates with a high density (>99.6%) were used as a sputtering target. The substrate was not intentionally heated. The films consisted of amorphous calcium phosphate and oxyapatite (Ca10(PO4)6O) phases. The ratio of the oxyapatite phase depended on the sputtering conditions of RF power, oxygen gas concentration in the sputtering gas (CO2) and total pressure in the chamber. The (002) preferred orientation of oxyapatite phase was observed. The deposition rate of films increased with increasing RF power and decreasing CO2. The highest deposition rate was 0.143 nm·s−1 (0.515 μm·h−1).

Content from these authors
© 2005 The Japan Institute of Metals and Materials
Previous article Next article
feedback
Top