2006 年 47 巻 11 号 p. 2867-2870
The superelastic properties of cast Ti-Ni shape memory alloy (SMA) were studied. Base materials were prepared as a melting method ingot and as a self-propagating high-temperature synthesis (SHS) ingot. The composition of these ingots was Ti-50.8 at%Ni. Each ingot was cast into a rod shape by centrifugal casting. The heat-treatment conditions were 773 K for-1.8 ks and 773 K–1.8 ks → 873 K–3.6 ks. Shape memory characteristics were measured by differential scanning calorimetry (DSC), X-ray diffraction (XRD) and a tensile test. All casting specimens have good shape memory characteristics. According to DSC measurements, the melt method specimens show gravity segregation.