2008 年 49 巻 12 号 p. 2887-2890
The effect of Cr addition on the glass-forming ability (GFA), the magnetic properties, and corrosion resistance of (Fe0.76Si0.096B0.096P0.048)100−xCrx (x=0, 2, 4 and 6) bulk glassy alloys (BGAs) with high Fe contents was investigated. 4% Cr addition makes the alloy composition to approach towards a eutectic point, which could result in an increase in the GFA. The BGA rod with diameters up to 3 mm was produced by copper mold casting. These BGAs exhibit a rather high saturation magnetization of 1.10–1.50 T and lower coercive force of 1.4–2.4 A/m. A significant improvement in corrosion resistance was observed with increasing Cr content. Furthermore, these Fe-based BGAs exhibit super high strength of ∼3.3 GPa and Young’s modulus of 168 GPa.