Alignment of Carbon Nanofibers in the Al2O3 Matrix under a Magnetic Field
2011 年 52 巻 3 号 p. 572-575
詳細
2011 年 52 巻 3 号 p. 572-575
A stable suspension of multi-walled carbon nanofibers (CNFs) in Al2O3 was prepared by adding ammonium polycarboxylate as a dispersant in an aqueous solution. A strong magnetic field of 12 T was applied to the CNFs/Al2O3 suspension to investigate the alignment of the CNFs. The result was that the CNFs in the matrix showed good alignment with the direction of the magnetic field. It was found that 0.5 mass% CNFs showed isolated alignment; in contrast, with 5 mass% CNFs there were mainly aligned bundles. The alignment was only seen with straight CNFs; curved CNFs showed no alignment in a magnetic field.