Effects of T5 Treatment on the Microstructure and Mechanical Properties of Mg-8Al-2Li Alloy

抄録

In this study, the effects of T5 treatment on the microstructure and mechanical properties of Mg-8Al-2Li specimens are investigated. The experimental results show the T5-treated Mg-8Al-2Li specimens will produce the β-Mg₁₇Al₁₂ and/or AlLi precipitates depending on the aging temperatures. The T5-treated Mg-8Al-2Li specimens will display an obvious precipitation strengthening, regardless of whether the precipitates are single β-Mg₁₇Al₁₂ phase or dual phases of AlLi and Mg₁₇Al₁₂. Their maximum tensile strengths can reach 355–375 MPa, which are 12–18% increment compared with that of the as-extruded specimen. Meanwhile, the T5-treated Mg-8Al-2Li specimens can still show good ductility with ∼9% elongation for specimens with their maximum strengths.