2011 年 52 巻 9 号 p. 1832-1835
Nano-powders of 1.5TiAl and Al2O3 were synthesized from 1.5TiO2 and 3.5Al powders by high energy ball milling. Nanocrystalline Al2O3 reinforced composite was consolidated by high frequency induction heated sintering within 2 min from mechanochemically synthesized powders of Al2O3 and 1.5TiAl. The relative density of the composite was 99%. The average hardness and fracture toughness values obtained were 1340 kg/mm2 and 9 MPa·m1⁄2, respectively.