2018 年 59 巻 7 号 p. 1068-1070
This study discusses the crystal structure and magnetic properties of the rare-earth doped La0.8R0.2(Fe0.88Si0.12)13 (with R = Sm, Tb) compounds. All the samples were prepared by using arc-melting technique in argon atmosphere and the obtained result shows that after heat treatment, the samples exhibited the NaZn13-type cubic phase with a small amount of a secondary α-Fe phase. The magnetic properties and magnetic entropy change were determined by mean of the temperature and field dependence magnetizations. Besides the decrease in the lattice constants, there was also observed a significant increase of Curie temperature and magnetic entropy change −ΔSM which reached a maximum of 4.5 J/kg K for La0.8Sm0.2(Fe0.88Si0.12)13, corresponding to a relative cooling powers (RCP) of 102 J/kg for the sample.