Effects of Electron Beam Irradiation on Elasticity of CFRTP (CF/PEEK)
Hiroaki TakeiMichelle SalviaAlain VautrinAkira TonegawaYoshitake Nishi
著者情報
ジャーナル 認証あり 早期公開

論文ID: MBW201005

この記事には本公開記事があります。
詳細
抄録
Homogeneous low voltage electron beam irradiation (HLEBI) improved the elasticity indicated by both flexural modulus (Ef) and the maximum slope value ((dσ⁄dε)max) of the bending stress–strain curve of carbon fiber reinforced thermoplastic polyetheretherketone (CFRTP) composite sheets with 0.50 mm thickness, although the penetration depth estimated was from 0.14 to 0.21 mm on both side surfaces. HLEBI remarkably enhanced both Ef and (dσ⁄dε)max. The Ef at middle cumulative probability (PE) of 0.50 for CFRTP irradiated at 0.30 MGy (kJg−1) was 3.3 GPa, which was 27% higher (2.6 GPa) than for CFRTP before irradiation. Moreover, (dσ⁄dε)max at middle cumulative probability (PE=0.50) was more than 4.9 GPa for CFRTP irradiated at 0.30 MGy. The interfacial friction force, as well as the strengthening of both carbon fiber and polyetheretherketone probably contributed to the HLEBI effects to enhance both Ef and (dσ⁄dε)max in the CFRTP.
著者関連情報
© 2011 The Japan Institute of Metals and Materials
feedback
Top