Electron microscope observation is carried out in and around {1\bar102} twins in lightly-stretched magnesium foils. Stacking faults are observed mainly in the twins and sometimes in the matrix around the twins. Identification of dislocations by two-beam bright-field electron microscopy shows that during deformation many (a+c) dislocations are produced within the twins.