Abstract
Zr55Al15Ni10Cu20 bulk metallic glass is formed using low purity materials at a low vacuum with a small amount of yttrium addition. It is found that the glass forming ability, crystallization and melting process of the Zr55Al15Ni10Cu20 alloy are modified with yttrium addition, while the mechanical and elastic properties, such as hardness and Young’s Modulus, are not obviously changed. The positive effect of yttrium addition on the glassy formation of the Zr55Al15Ni10Cu20 alloy is clarified.