Covalent organic framework (COF) films were synthesized from the vapor phase. The films annealed at 400 ℃ had a pore network structure with a diameter of 2.9 ～ 3.5 nm. Experimental and numerical analysis show that the COF was more permeable to CO2 than N2 due to its greater affinity for CO2 compared to N2