炭酸カルシウムと水酸化カルシウムの混合物を加熱して得た酸化カルシウムの焼結性
吉松 英之河内 慶子上野 覚村岡 賢三浦 嘉也
著者情報
ジャーナル フリー

2000 年 7 巻 286 号 p. 172-177

詳細
抄録

Sinterability of CaO prepared from Al2O3 coated CaCO3-Ca (OH) 2 powder was investigated in order to clarify effect of Ca (OH) 2 and small amount of Al2O3 content.The CaCO3-Ca (OH) 2 mixed powders were coated with a chelate compound of aluminum corresponding to 0-0.1mass%Al2O3. The CIP'ed compacts of the powders were sintered at a rate of 300°C·h-1 up to 1500°C in air and held at 1500°C for 2h to prepare CaO ceramics. The bulk density and fine structure for the CaO ceramics were measured in process of sintering. The bulk density for the CaO ceramics prepared from CaCO3-Ca (OH) 2 mixed powder was higher than that from CaCO3 powder at the temperature above 800°C. The bulk density of the CaO ceramics was slightly increased with increase of Al2O3 content, while the CaO grain size was greatly increased with Al2O3 content.

著者関連情報
© 無機マテリアル学会
前の記事 次の記事
feedback
Top