P9 水溶液中におけるメチルセルロースの超音波切断に関する研究(ポスターセッション)
田口 君彦松岡 辰郎香田 忍
著者情報
会議録・要旨集 フリー

詳細
抄録

The mechanism of ultrasonic degradation is still obscure, but it is well accepted that cavitation bubbles are mainly responsible for the degradation. The intense shear field generated by the collapse of the cavitation bubbles induces chain scission. Most of investigations on ultrasonic degradation have been carried out at low ultrasonic frequency around 20kHz. In this work, the ultrasonic degradation of methyl cellulose in aqueous solution was studied at two frequencies (20kHz and 500kHz) at the constant calorimetric power (20W) and temperature (25℃). The time variation of the average molecular weights and the molecular distribution were determined by Gel Permeation Chromatography (GPC). The mass average molecular weights (M_w) decreases with sonication time. The large lowering of M_w was observed at the frequency 500kHz. The degradation rate was suppressed by the addition of t-BuOH which act as a radical scavenger. The ultrasonic degradation rate coefficient k_d was estimated and compared with the results of other water-soluble polymers. The order of k_d value were PEO > Dextran 〓 Pullulan > MC. We will discuss on the frequency effects on the ultrasonic degradation.

著者関連情報
© 2006 日本ソノケミストリー学会
前の記事 次の記事
feedback
Top