抄録
In order to identify the mechanism originating the threshold stress for the high-temperature deformation of dispersion-strengthened alloys, stress-change tests were conducted during deformation of an Al-1.5 vol%Be alloy. It was found that the instantaneous strain on the increase in applied stress was absolutely elastic when the stress-increment Δσ was below a certain value Δσc, an instantaneous plastic strain was observed for Δσ>Δσc, whereas the strain was always elastic for a stress-decrement. The critical stress Δσc depended on temperature and showed a maximum in a temperature range from 570K to 620K. From these findings it is discussed that the threshold stress should be determined by the Srolovitz mechanism.