Effect of Coating Crystal Orientation and Mineral Mist on Adhesion Phenomenon

Abstract

Effect of coating crystal orientation and mineral water mist on adhesion phenomenon were researched. As for the Belag formation, the coated film with (111)-oriented rich had more adhesion than (200)-oriented rich coated film, compared with both orientations. On the other hand, the mineral water mist machining was performed for face milling of Ti-6Al-4V and Inconel 718. The reduction of adhesion of work material and the suppression of wear were observed when applied the mineral water mist.