Abstract
The behavior and composition of a cathode film formed on a steel cathode during chromium plating were studied with radioactive tracers. A special cell with a rapid washing compartment was used for preventing the cathode film from dissolving in electrolyte after plating. The cathode film was composed of two layers. The outer layer facing to the electrolyte had a loose structure and contained more sulfuric anions than the inner layer, for sulfuric acid probably concentrated in the outer layer. This outer layer is called L-film in this paper. The L-film was easily dissolved in the electrolyte solution. The inner layer (called C-film, compact film) was stable against electrolytes and contained less anions than that of L-film. The C-film had a thickness equivalent to 5mg/m2 and the concentration of anions unaffected by the composition of electrolytes. The C-film was not reduced to metallic chromium, but it remained in the cathode film during and after plating. This suggests that chromic acid in the cathode film is not reduced to metallic chromium, that metallic chromium is deposited from chromium complexes reaching the cathode surface through the cathode film, and that the complexes do not play a role on the construction of the cathode film.