Effect of Ultrafine Powder of Hematite and Magnetite on Granulation Characteristics of Iron Oxide
Takayuki MaedaYuhei HayashiKo-ichiro OhnoKazuya Kunitomo
Author information
JOURNAL OPEN ACCESS FULL-TEXT HTML

2017 Volume 103 Issue 6 Pages 246-253

Details
Abstract

Effect of ultrafine powder of Hematite and Magnetite on granulation characteristics of iron oxide was investigated by mixing and exterior coating granulation. The results obtained are follows:

(1) In the case of Hematite Ore H, particle diameter of granule is increase with increasing the amount of fine powder in both mixing granulation and exterior coating granulation. On the other hand, in the case of Magnetite Ore M, particle diameter of granule is increase with increasing the amount of fine powder in mixing granulation. In the case of exterior coating granulation using Magnetite Ore M, particle diameter of granule is increase with increasing until 20 mass% of added fine powder but particle diameter of granule is decrease when the amount of fine powder added 30 mass%.

(2) The particle diameter dependence of wet strength is relatively small in both mixing and exterior coating granulation. Except for 30 mass% of added fine Magnetite ore M in exterior coating granulation, wet strength of granule is not increase even if the amount of added fine Hematite Ore H and Magnetite ore M is increase. Therefore, it is considered that wet strength of granule is determined by adhesion force of liquid bridge.

(3) In mixing granulation, the particle diameter dependence of dry strength is relatively small. In the case of exterior coating granulation, dry strength of granule is decrease with increasing the particle diameter of granule. The dry strength of granule made from mixing granulation is larger than that of exterior coating granulation.

Content from these authors
© 2017 The Iron and Steel Institute of Japan

This article is licensed under a Creative Commons [Attribution-NonCommercial-NoDerivatives 4.0 International] license.
https://creativecommons.org/licenses/by-nc-nd/4.0/
Previous article Next article
feedback
Top