フェライト系ステンレス鋼の等軸晶生成に及ぼすマグネシウム添加の影響
2012 年 98 巻 11 号 p. 601-609
詳細
2012 年 98 巻 11 号 p. 601-609
Effect of Mg and Ti addition on the solidification macrostructure of ferritic stainless steel was evaluated in order to obtain the fine equiaxed grains. Equiaxed solidification was promoted by adding Mg and Ti. Ti addition affects the amount of TiN as a nucleation agent of δ-Fe and the increase in constitutional undercooling. Mg addition produces Spinel oxide in the molten steel, which accelerate the TiN formation. [Al] content also have an influence on the equiaxed grain formation.