TiO2を含有する鉱滓による微細化黒鉛鋳鉄に関する研究(IX)
S-H鋳鉄の網目組織ならびに微小硬度測定
沢村 宏津田 昌利
著者情報
ジャーナル フリー

1957 年 43 巻 12 号 p. 1286-1293

詳細
抄録

The fracture surface as well as the polished surface of S-H cast iron shows a net structure having a boundary line of light gray color. The microstructure proved that the boundary-line portion was a group of austenite dendrite and that the mesh of net (meshy portion) was consisted of eutectic graphite structure.
Both the micro-hardnesses of boundary-line and meshy portions were estimated. The results proved that the hardness of boundary-line portion was about 1.5-2.7 times of meshy portion.
The authors presumed that one of the major reasons of the greater wear-resistance of S-H cast iron was based upon the following characteristics:
1. The existence of a unique net structure of S-H cast iron.
2. The presence of a boundary-line portion of greater hardness in the matrix of eutectic graphite structure of lower hardness.
3. The fine and uniform distribution of fine TiC particles in S-H cast iron casting.