1989 年 75 巻 9 号 p. 1604-1611
The addition of Mo2CoB2 and TiH2to the TiB2 improved the density, the bending strength and other properties. Especially, the additions of 15wt %Mo2CoB2 and 2wt %TiH2 brought the highest bending strength as 149 kgf/mm2 and high hardness as HV2 800. Sliding wear test against mild steel showed that TiB2-TiH2-Mo2CoB2 ceramics have relatively little specific wear rates compared with SiC, Si3N4, ZrO2 but have large specific, wear rates compared with Al2O3 and cemented carbides (D10). Specific wear rates of TiB2 based ceramics could be decreased less than Al2O3 and cemented carbides (D10) by the addition of TiC0.7N0.3 without lowering the bending strength. Furthermore this ceramics have good abrasive wear resistance.