真空蒸着による自溶性ろう材の液相拡散接合性
1996 年 82 巻 6 号 p. 509-513
詳細
1996 年 82 巻 6 号 p. 509-513
The transient liquid phase bonding (TLP bonding) has been studied on a Hastelloy X whose surface is ion-plated with a self-melted tertiary alloy of a Ni-15mass% Cr-B alloy. The ion-plated coat filler contains about 2 to 4mass% boron as a melting point depressant. The thickness of the filler metal is from 3 to 12μm. It was found that the diffusion zone is narrow and the joint strength is insufficient when the content of boron is low and the thickness of a filler is thin. However, the joint strength increases sharply when the thickness reaches about 7μm. These facts were discussed on the basis of microstructural observation, the distribution of diffusion elements and the isothermal solidification time of a thin filler.