スラグ共存下のAl脱酸過程におけるステンレス溶鋼中スピネル介在物の生成
西 隆之眞目 薫
著者情報
ジャーナル オープンアクセス

1998 年 84 巻 12 号 p. 837-843

詳細
抄録
Morphology change of inclusions were experimentally investigated under Al deoxidation of molten stainless steel with CaO-SiO2-Al2O3-MgO slags in order to clarify the morphology control factor of inclusions. 15kg of molten 18mass%Cr-8mass%Ni stainless steels were deoxidized by aluminum at 1873K, and the samples were taken at intervals to observe the inclusions by SEM and EDS. As the results, MgO contents of alumina type inclusions were gradually increased with time and the maximum contents were affected by a CaO/SiO2 ratio in slags. The formation of MgO-Al2O3, spinel type inclusions were also observed in case of high CaO/Si02 ratio. The origin of Mg in inclusions was presumed to be deformation of MgO in slags.
著者関連情報
© 一般社団法人 日本鉄鋼協会

This article is licensed under a Creative Commons [Attribution-NonCommercial-NoDerivatives 4.0 International] license.
https://creativecommons.org/licenses/by-nc-nd/4.0/
次の記事
feedback
Top