鉄鉱石からの還元鉄のCO-H2-H2S混合ガスによる炭化鉄生成速度
堀井 一良井口 義章林 昭二守屋 健
著者情報
ジャーナル フリー

2003 年 89 巻 10 号 p. 1011-1017

詳細
抄録

The rate of iron carbide formation by the reaction of completely reduced limonite with CO-H2-H2S mixtures of as=0.5 was gravimetrically measured. The weight gain by the reaction was evidenced to directly correspond to the carburization, i.e. taking in carbon from the gas phase, to form iron carbide by comparing the weight gain with the amount of carbon in iron carbides analyzed by Mossbauer spectroscopy. The rate was measured in the varied total flow rates and varied compositions of the reaction gas, and the varied weight and varied size of iron ore particles. It was concluded that the carburization rate on pore surface of completely reduced iron ore particles controls the iron carbide formation rate. By applying the integrated rate equation for the first order reaction to fθ versus t curves, the carburization rate was evaluated. The rate of the reduced limonite ore was much faster than the rate of a reduced hematite ore by the factor about 6. From the rate being nearly proportional to pCO to 80%CO, it was concluded that the main carburization reaction is CO+H2=[C]+H2O and the rate controlling step is the dissociative adsorption of CO molecules. The carburization rate decreased with increasing the reduction temperature but it hardly changed with the carburization temperature because the rate was strongly dependent on the specific surface are of reduced limonite. The dependencies of the rate on the reduction temperature for the carbide formation at 973K and on the carbide formation temperature from the reduced limonite at 1173K were quantitatively discussed.

著者関連情報
© 一般社団法人 日本鉄鋼協会
前の記事 次の記事
feedback
Top