As a result of examination on the hexavalent chromium sorption behavior of calcium aluminate, the following results have been obtained. Each type of calcium aluminate sorbs hexavalent chromium in liquid phase according to hydration. The hexavalent chromium decreasing rate of calcium aluminate is larger than that of OPC or BB, and its sorption capacity is also large. According to estimation of Cr sorption capacity per gram of various of calcium aluminates, the following results were obtained : ca. 65 mg for CA, ca. 98 mg for C₁₂A₇, and ca. 152 mg for C₃A. When calcium aluminate sorbs Cr according to hydration, it takes Cr into the hydrated product in an intact form of hexavalent chromium. Formation of CrO₄^2-type U-phase was confirmed in a case of high Cr concentration. The cause of this was considered due to that in a system with high Cr concentration, by main component of Cr standard solution is K₂Cr₂O₇, also the addition of sodium hydroxide for controlling pH to neutral state, both of alkali metal ion and CrO₄^2-concentration became high. Compared with calcium silicate, OPC and BB, calcium aluminate is resistant to the leaching of hexavalent chromium that was sorbed according to hydration, which leads to its excellency in holding ability for hexavalent chromium.

抄録全体を表示

5mass%のセッコウを添加して, トバモライト成形体を180℃の蒸気中で作成した.この成形体はセッコウ無添加の場合と同じように820℃でウォラストナイトとシリカへと分解し, 成形体は収縮した.しかし, 5mass%のセッコウを添加するにより収縮量は14%から10%へ低下した.この原因は, セッコウを添加したことによりトバモライト結晶が大きく成長して成形体内に大きな気孔が形成され, 熱分解と同時に生ずる焼結にともなう収縮が軽減されたためと考えられる.

抄録全体を表示