Article ID: 2020-023
The purpose of this study is to clarify physical and chemical changes in surfaces of CAD/CAM composites caused by alumina airborne-particle abrasion and its effect on adhesive bonding. Our study involved three dispersed filler (DF)-based and a polymer-infiltrated ceramic network (PICN)-based CAD/CAM composites. Changes in the surface morphologies of the composites were examined, and surface free energy (SFE) analysis was performed based on Owens-Wendt theory. The influence of the abrasion on the bond strengths of CAD/CAM composites to the resin cement was characterized by shear bond strength (SBS) test. The abrasion increased the roughness of the composites. The SFE analysis showed that the abrasion significantly increased the dispersive component but decreased the polar component of the SFE associated with the DF-based composites, while no change occurred for those of the PICN-based composite. The abrasion slightly improved the SBSs for the DF-based composites but not that of the PICN-based composite.