論文ID: 2024-195
This study aimed to evaluate ionic release, flexural strength and water absorption of UDMA resins containing 0–30 wt% surface pre-reacted glass-ionomer (S-PRG) filler fabricated by a DLP 3D printer. Release of Al, B, Na, Sr and F ions were measured by inductively coupled plasma (ICP) and an ion meter. Flexural strength test and water absorption measurements were performed according to the International Organization for Standardization (ISO) 4049 standard and ISO 1567 standard, respectively. Sr ions were released the most, followed by F, B, Na and Al ions. The highest flexural strength was recorded with the S-PRG filler amount 0 wt%, followed by the S-PRG filler amounts 30, 20 and 10 wt%. Water absorption after one week was below the 32 µg/mm3 mark specified by ISO 1567. The release of ions was confirmed using UDMA-based photopolymerized resin containing S-PRG filler. Furthermore, the results suggest that this resin could be used for provisional restoration.