抄録
A study to achieve high-strength, high porosity and permeability pervious concrete pavement was carried out. Mix proportions in terms of cement content, coarse aggregate-cement ratio (CA/C) and water-cement (W/C) ratio were varied. A mix proportion providing the optimal combination of strength and porosity was chosen, and polymer superplasticizers were added to examine their effect on the strength and porosity. Results showed that a water-cement ratio of 0.2 resulted in a dry and brittle mix that led to compressive strength less than 15MPa but a high permeability rate of approximately 20mm/s. A mix with w/c ratio of 0.3 and CA/C ratio of 4.25 resulted in compressive strength of 13.9MPa, flexural strength of 3MPa and high porosity of more than 20%. The use of high cement content of 495kg/m3 in the mix resulted in high compressive strengths of 51.8MPa, flexural strength of more than 4MPa, however permeability was reduced to approximately 1mm/s.