抄録
Fuel cross leak through a polymer electrolyte membrane of the direct dimethyl ether fuel cell (DDFC) was investigated and was found to be approximately one-tenth that of the direct methanol fuel cell (DMFC). Three phenomena known to appear in the DMFC were also observed in the DDFC. These were (1) fuel cross leak due to the diffusion which increases with the fuel concentration on an open circuit condition, (2) electro-osmotic cross leak, which increases with the current density and fuel concentration, and (3) decrease of fuel cross leak with the increase of the current density due to fuel consumption at low fuel concentration. The decreased fuel cross leak realized by using Nafion ®117 as a membrane and the low fuel concentration of 11% resulted in an increase of the Farady efficiency of the DDFC of up to 90% at a current density of 80mA/cm2. The CO2 quantity at the anode outlet of the operating DDFC was slightly less than 2 mol per 12 protons, as estimated from an electrochemical reaction on the anode. The CO2 quantity at the cathode outlet was also investigated. The CO2 cross leak increased with current density at every CO2 concentration and the diffusion appeared to be the dominant phenomenon of the CO2 cross leak.