2019 年 59 巻 5 号 p. 872-879
In the current study, the solidification structure, non-metallic inclusions and hot ductility of continuously cast high manganese TWIP steel slab have been investigated and the inclusion formation behavior have been revealed by FactSage (CRCT-ThermFact Inc., Montréal, Canada). The area ratio of equiaxed grain zone of the TWIP steel slab is 0.18. Two main types of inclusions in the TWIP steel slab are single AlN particle and AlN+MnS aggregates. It is found that MgAl2O4 and AlN particles can precipitate in the initial solidification stage, which can act as heterogeneous nuclei of other inclusions. In the high temperature tension test, the reduction of area (RA) of the TWIP steel slab samples are higher than 40 pct in the temperature range from 873 K to 1473 K (600°C to 1200°C). Brittle fractures are observed in the fracture surface of the TWIP steel slab samples with dimples. Contents of manganese, carbon, sulfur and phosphorus, strain rate, and dynamic recrystallization (DRX) are factors influencing the hot ductility of TWIP steel slab.