1999 年 107 巻 1251 号 p. 1037-1040
Sol-gel derived P2O5-SiO2 glasses were studied and a remarkable improvement in protonic conduction was observed by increasing the P2O5 content. This was attributed to (1) the variation in glass structure including the reduction of the degree of cross-linking skeleton and the increase of specific surface area of glass due to the non-bridging oxygen (P=O) in P-O tetrahedron, (2) the formation of stronger hydrogen bond between hydroxyl group and P=O group as well as hydroxyl group and, (3) the p-π resonance effect in O(3-t)PO(OH)t unit.