Tough and dense boron carbide obtained by high-pressure (300 MPa) and low-temperature (1600°C) spark plasma sintering

抄録

Dense boron carbide (above 95%) was achieved through high pressure (300 MPa) and low temperature (1600°C) Spark Plasma Sintering (SPS). This approach resulted in improvement of fracture toughness and of dynamic toughness when compared to corresponding toughness values of the sample sintered by conventional SPS (2100°C, 50 MPa). Dynamic toughness was extracted from Split Hopkinson Pressure Bar measurements. Results are understood based on microstructure and on very different behaviour of the samples in respect to residual B₂O₃ and carbon available in the raw B₄C powder.