Synthesis of silicon carbide nanoplates by using laboratory wastes as resource at low temperature

Yongjie Xie; Zixun Huang; Qingting Ni; Shunkai Wang; Lin Ban; Taotao Yun; Jiali Dai; Liangbiao Wang; Xiaokai Song

doi:10.2109/jcersj2.22094

Notes

Synthesis of silicon carbide nanoplates by using laboratory wastes as resource at low temperature

Yongjie Xie, Zixun Huang, Qingting Ni, Shunkai Wang, Lin Ban, Taotao Yun, Jiali Dai, Liangbiao Wang, Xiaokai Song

著者情報

Yongjie Xie
Jiangsu Key Laboratory of Precious Metals Chemistry and Engineering, School of Chemistry and Environment Engineering, Jiangsu University of Technology
Zixun Huang
Jiangsu Key Laboratory of Precious Metals Chemistry and Engineering, School of Chemistry and Environment Engineering, Jiangsu University of Technology
Qingting Ni
Jiangsu Key Laboratory of Precious Metals Chemistry and Engineering, School of Chemistry and Environment Engineering, Jiangsu University of Technology
Shunkai Wang
Jiangsu Key Laboratory of Precious Metals Chemistry and Engineering, School of Chemistry and Environment Engineering, Jiangsu University of Technology
Lin Ban
Jiangsu Key Laboratory of Precious Metals Chemistry and Engineering, School of Chemistry and Environment Engineering, Jiangsu University of Technology
Taotao Yun
Jiangsu Changli Testing Service Co., Ltd.
Jiali Dai
Jiangsu Guorun Testing Service Co., Ltd.
Liangbiao Wang
Jiangsu Key Laboratory of Precious Metals Chemistry and Engineering, School of Chemistry and Environment Engineering, Jiangsu University of Technology
Xiaokai Song
Jiangsu Key Laboratory of Precious Metals Chemistry and Engineering, School of Chemistry and Environment Engineering, Jiangsu University of Technology

キーワード: Silicon carbide, Nanoplates, Chemical synthesis, X-ray methods

ジャーナルフリー

2022 年 130 巻 12 号 p. 943-947

DOI https://doi.org/10.2109/jcersj2.22094

詳細

抄録

In this study, silicon carbide (SiC) nanoplates are prepared from the waste quart tube (main composition: silicon dioxide) and waste autoclave lining (main composition: polytetrafluoroethylene) produced in the laboratory. The reaction is carried in a stainless steel autoclave at 600 °C through a magnesium reduction route. Electron microscopy investigations show that the nanoplate thickness of the SiC sample is about 20 nm, and the edge length is about 200 nm. Furthermore, the photoluminescence property of the obtained SiC nanoplates is investigated.