HIPおよびRHIPにより固化処理したCr粒子添加強化型NiAl金属間化合物の特性
2004 年 68 巻 9 号 p. 831-837
詳細
2004 年 68 巻 9 号 p. 831-837
NiAl intermetallics with dispersive Cr particles consolidated by the Hot Isostaic Press (HIP) and Reactive HIP (RHIP) techniques, has been investigated. Mechanical properties of HIPed and RHIPed materials with various Cr concentrations ranging form 0 to 30 mass%Cr, were examined at various temperatures. The consolidation temperature of RHIP materials decreases with Cr addition; when RHIPing NiAl+xCr compounds with 25 mass% has attained, remarkable high ductility over 17% elongation and over 400 MPa tensile strength at 873 K. A very high tensile strength of HIPed NiAl+20 wt.%Cr about 600 MPa with 10% elongation was achieved at 673 K.