2007 年 71 巻 3 号 p. 326-329
The addition of 2 at%Mo combined with 2 at%Si was found to be effective for the extension of the supercooled liquid region (ΔTx) and approaching alloy to a eutectic point in the Fe77-xMoxGa3P10C4B4Si2 alloy system. The ΔTx value is 33 K for the Fe77Ga3P12C4B4 glassy alloy, and increases to 60 K for the Fe75Mo2Ga3P10C4B4Si2 glassy alloy. Besides, this glassy alloy exhibits a high reduced glass transition temperature (Tg/Tl) of 0.6. The large ΔTx and high Tg/Tl enabled us to prepare the Fe75Mo2Ga3P10C4B4Si2 bulk glassy alloy successfully with a diameter of 2 mm and high saturation magnetization (Is) of 1.27 T. The Fe75Mo2Ga3P10C4B4Si2 glassy alloy also exhibits good soft magnetic properties, i.e., high effective permeability at 1 kHz of 1.1×104 and low coercive force of 5 A/m.