光コヒーレンストモグラフィーによるセラミックス焼結体とスラリーの内部構造観察

抄録

Optical coherence tomography (OCT) is an observation technique utilizing optical interferometry. Images of the internal structure of opaque materials can be obtained dynamically and three-dimensionally in a few seconds. In this work, the internal structures of ceramic sintered body and slurry was observed by OCT. In the case of Al₂O₃ ceramics, an artificially induced spherical defect having smaller than 50 µm in diameter which lies 700 μm below the top surface was observed successfully. Furthermore, it was observed that the internal structure of Al₂O₃ slurry was drastically changed during drying, followed by formation of a crack in the dried green body.