2023 Volume 72 Issue 3 Pages 347-356
For practical applications such as fuel cells, it is important to exploit electrocatalysis with high activity for methanol and glycerol oxidation. A platinum nanostructured electrode (PtNPs) is modified by gold adatoms and is created by application of a square wave potential regime to a tantalum surface electrode. In nanostructured platinum, the structure and the surface properties are characterized by scanning electron microscopy (SEM), X-ray powder diffraction (XRD) and cyclic voltammetry (CV). In acid and alkaline media, the CV and Chronoamperometric (CA) are studied to investigate the catalytic activity of the PtNPs nanoparticles for the electrooxidation of methanol and glycerol. The prepared nanostructured platinum on a tantalum electrode was allowed to balance an open circuit with a 1.0×10-3 M solution containing an Au ion. Consequently, the proximity of the irreversibly adsorbed Au-adatoms on the already described Pt-nanostructured electrode. In acidic and alkaline solutions, the electrocatalytically activities toward methanol and glycerol oxidation were evaluated and is found to strongly on the surface of the gold-modified PtNPs. The PtNPs modified by Au electrode system used direct methanol fuel cell (DMFC) and direct glycerol fuel cell (DGFC). The DMFC and DGFC are much higher than in acid output in alkaline. Comparison of the i-E curves of nanostructure platinum electrode with that of a platinum nanostructure electrode modified by Au under similar conditions for the letter, the charge under the peak (i-E curve) in the oxidation region was higher. Furthermore, rough chronoamperometric measurements confirmed the results. The results of showed that the electrocatalytic properties of the nanostructured prepared surface were enhanced by the inclusion of gold adatoms with a variable extent of advancement. The current peak (Ip) and the current chronoamperometric (ICA) of glycerol oxidation on the PtNPs electrode modified by Au in acid media (130 mA/cm2, 47 µA/cm2) were higher than those of the bare PtNPs electrode and in alkaline media (171 mA/cm2, 66 µA/cm2). The stronger catalytic behavior in alkaline media of the Au-PtNP electrode indicates its promising use in alkaline direct alcohol cells.