Effect of noble metal adhesive systems on bonding between an indirect composite material and a gold alloy

Abstract

In this study, the bond strength between an indirect composite and a gold alloy was determined for the purpose of evaluating noble metal bonding systems. A single liquid primer designed for conditioning noble metal alloys (Infis Opaque Primer) and tri-n-butylborane-initiated adhesive resins (Super-Bond C & B), with or without the powder component, were assessed. Cast gold alloy disks (Casting Gold type IV) were air-abraded with alumina, followed by six surface preparations, and were then bonded with a light-activated composite material (New Metacolor Infis). Shear testing was performed both before and after thermocycling for evaluation of bond durability. The results showed that three primed groups improved post-thermocycling bond strengths compared to each of the corresponding unprimed groups (P < 0.01). The bond strength was reduced for all six groups by the application of thermocycling (P < 0.01). After thermocycling, the group primed with the Infis Opaque Primer material and bonded with the Super-Bond C & B resin exhibited the greatest bond strength (23.4 MPa). The Infis Opaque Primer and Super-Bond bonding system increased the post-thermocycling bond strength of the control group by a factor of approximately ten. This simple technique is applicable in the fabrication of composite veneered restorations and cone-telescope dentures. (J. Oral Sci. 46, 235-239, 2004)