2019 Volume 63 Issue 2 Pages 145-149
Purpose: The aim of this study was to evaluate the shear bond strength and durability of MMA-TBB resin to human enamel applied a self-etching primer with phosphoric acid etching.
Methods: A self-etching primer (Teeth primer, TP) containing 4-methacryloyloxyethyl trimellitate anhydride (4-META) and sodium sulfite and two etchants having different phosphoric acid concentrations (K-etchant gel, KE, 35–45%: Red gel, RG, 20–25%) were used as treatment agent, and MMA-TBB resin was used as luting agent. Enamel surfaces were treated with six methods which were as follow: KE, RG, TP, KE + TP, and RG + TP. After enamel specimens were bonded with MMA-TBB resin and stored in distilled water for 24 h, the shear bond strength test was done at 0 thermocycling or 20,000 thermocycling. These results were statistically verified with Steel-Dwass multiple comparisons and Man–Whitney U test.
Results: The shear bond strength of TP group, KE + TP group, and RG + TP group were significantly higher than KE group and RG group in pre-thermocycling. KE + TP group and RG + TP group were significantly higher than other groups in post-thermocycling.
Conclusions: Applying TP with phosphoric acid etching can increased shear bond durability despite difference of phosphoric acid concentrations (35–45% or 20–25%).
This article cannot obtain the latest cited-by information.