Irradiation therapy and chewing simulation: effect on zirconia and human enamel

Abstract

Purpose: Ionizing radiation therapy (RT) is the main option for head and neck cancer treatment, but it is associated with multiple side effects. This study aimed to evaluate the effect of RT associated with chewing simulation on the surface of human enamel and Yttria-partially stabilized zirconia (Y-TZP).
Methods: Maxillary premolar cusps and Y-TZP slabs were divided in 7 experimental groups: CO: no RT (control); EZ groups had irradiation applied to both, enamel and zirconia samples (simulating restoration prior to RT); E groups had irradiation applied to enamel only (simulating restoration after RT). RT doses were either 30, 50 or 70 Gray (Gy). Enamel cusps were abraded against zirconia slabs in a chewing simulator (CS - one million cycles/ 80 N/ 60 mm/min, 2 mm horizontal path, artificial saliva, 37˚ C). Zirconia hardness was evaluated before CS; zirconia roughness and enamel volume (wear) were evaluated before and after CS. Hardness and wear data were analyzed by one-way Analysis of Variance and Tukey post hoc test. Roughness was analyzed by Repeated Measures test and Bonferroni test (p=0.05).
Results: There was no significant effect of enamel or zirconia irradiation on enamel cusp wear (p=0.226), regardless of the irradiation dose used - up to 70 Gy. Irradiation also did not affect Y-TZP surface roughness (p=0.127) and hardness (p=0.964).
Conclusions: RT does not promote significant changes to the surface characteristics of zirconia. Irradiated enamel abraded against zirconia does not show higher wear volume when compared to non-irradiated enamel.