抄録
Penetration of H2 and CO2 through organic silicone compound sheet was tested from the viewpoint of gas separation. Additionally LaNix was deposited on the organic silicone compound sheet and the penetration characteristics of both H2 and CO2 were investigated. While almost no difference was observed at H2 and CO2 penetration through the sheet without LaNix, however, decreased hydrogen diffusion rate was measured for the film with LaNix.