Photo-rechargeable battery was constituted using the Pori-Pyrrole and Rhodaminine B as a photocatalyst layer and an electronic accumulation material respectively. Accumulation voltage and efficiency were measured with different polymerization voltage of 0.5-3.0[V]. At lower polymerization voltage, higher photo voltaic efficiency was obtained.