抄録
We have proposed a method on helical formation of coated nanowire, which utilized the misfit strain of the film coated on the nanowire. We also adopted a heat treatment that induces a creep flow only in the nanowire and thereby released the constraint of the nanowire on elastic bending due to film strain. In this study, we evaluate the magnetic field of Pt-coated CuO microcoils formed by using the method. A direct current is supplied to the coil on Au electrodes, and the voltage of the coil is measured using four-point probe method. The coil is melted due to a possible reason of joule heating at a current of 700 μA. The measured voltage increases proportionally to the increasing current until the current is 580 μA. Then, the voltage irregularly increases until the electrical discontinuity. We predict that the density of magnetic flux of the coil is 1.2 G at the current of 580 μA. This magnetic field is 3〜4 times of the geomagnetism.