摩擦攪拌インクリメンタルフォーミング法における成形形状測定結果を利用した成形性向上
大津 雅亮後藤 広志岡田 将人吉村 英徳松本 良村中 貴幸
著者情報
会議録・要旨集 認証あり

詳細
抄録

In friction stir incremental forming, formed shape becomes a little smaller than objective one due to springback. To improve forming accuracy, tool path was modified by experimentally obtained calibration equation. A5052 aluminum alloy sheets which size was 150 mm x 150 mm x 0.5 mm were employed for specimen. A hemispherical tool with a diameter of 6 mm was used. The tool was rotated at 10000 rpm and moved at 3000 mm/min and sheets were formed into a frustum of conical shape which height of 20 mm and wall angle of 25 °. Distance from the edge of blank holder to start position of forming was changed and errors of initial diameter of a frustum of cone, forming height and bottom diameter were measured. Errors of wall angle and overall shape were measured due to springback. By modification of tool path, errors of initial diameter, forming height, bottom diameter and wall angle were improved from 7.62 mm to 0.23 mm, 4.76 mm to 0.16 mm, 2.27 mm to 0.27 mm and 1.09 ° to 0.12 °, respectively.

著者関連情報
© 2016 一般社団法人 日本機械学会
前の記事 次の記事
feedback
Top