フレッティング疲労に及ぼす水素ガス環境の影響
久保田 祐信納山 尚樹笛田 宗広栄 中近藤 良之
著者情報
ジャーナル フリー

2005 年 54 巻 12 号 p. 1231-1236

詳細
抄録

The objective of this study is to clarify the effect of hydrogen gas environment on fretting fatigue strength of the materials, which will be used for the mechanical system for hydrogen utilization. It is important to take fretting fatigue into account for strength design, since many fatigue failure accidents have occurred at joints or contact parts between components. The test materials were austenitic stainless steel SUS 304 and corrosion resisting aluminum alloy A6061. Fretting fatigue tests and also fretting wear tests were done in hydrogen gas, nitrogen gas and air. Fretting fatigue strength in hydrogen gas environment was lower than that in air for both materials. Tangential force coefficient in hydrogen gas was larger than that in air. The appearance of fretting pit and microcrack was quite different among environments. Absorption of hydrogen was detected in contact pad of fretting wear test fretted in hydrogen gas environment. Fretting fatigue life of the stainless steel was decreased due to hydrogen pre-charge.

著者関連情報
© 2005 日本材料学会
前の記事 次の記事
feedback
Top