The finite element method was applied to a generation phase analysis for stable crack growth in inhomogeneous materials. Experimental data on stable crack growth in bimaterial CT specimens, which were composed of a base metal and a weld metal, were numerically simulated using the node -release technique, and the variations of the fracture mechanics parameters such as J-integral, T*-integral, J-integral and CTOA were calculated. The effects of the fusion line and the weld on the near crack fracture mechanics parameters were discussed.