環状切欠材のクリープ変形挙動と寿命推定
1997 年 63 巻 612 号 p. 1737-1743
詳細
1997 年 63 巻 612 号 p. 1737-1743
No method with which to characterize and/or illustrate total creep behavior for specimens with notches, holes or cracks has been proposed. In this paper it is proposed that most creep curves can be drawn with a master curve for each creep test whenever test conditions and failure modes are similar to each other, and the lifetime ratio normalized by the rupture time is introduced. Using smooth and circumferentially notched specimens of 2.25 Cr-1 Mo steel, creep tests were performed at 600°C for examination of this concept. Furthermore, a θ projection method was used to describe creep curves for notched specimens and to extrapolate longer creep lives. Then, the whole creep curve shape for notched specimens could be easily drawn, except for that in the vicinity of the rupture point. However, longer creep lives of notched specimens were underestimated in comparison with a simple extrapolation of the experimental data. This resulted from the negative dependence of the parameter of θ3 on the applied stress.