2002 年 43 巻 3 号 p. 410-413
Ti–Cr–V alloys are known to absorb protium up to H/M=2. However, Ti–Cr–20 at%V alloys with more than 56 at%Cr content were found to absorb up to H/M=1. This paper aims to make clear the effects of compositions on formations of 1, 2 protorides in Ti–Cr–V alloys, and the structure of the mono-protorides. It was found that the mono-protorides with fcc and hcp structures exist. The mono-protoride with the fcc structure was different from the di-protoride with the FCC structure in the lattice constants. Some relationship between appearance of the mono-protorides and disappearance of the plateau regions in low hydrogen pressure regions was considered to exist. As a result, the appearance regions of 1, 2 protorides in Ti–Cr–V alloys were derived.