Fatigue of Welded Magnesium Alloy Joints

Masato Tsujikawa; Hidetoshi Somekawa; Kenji Higashi; Hayato Iwasaki; Takeshi Hasegawa; Akiyoshi Mizuta

doi:10.2320/matertrans.45.419

Masato Tsujikawa, Hidetoshi Somekawa, Kenji Higashi, Hayato Iwasaki, Takeshi Hasegawa, Akiyoshi Mizuta

著者情報

キーワード: magnesium alloy, tungsten inert gas arc welding, friction stir welding, fatigue strength, crack propagation

ジャーナルフリー

2004 年 45 巻 2 号 p. 419-422

DOI https://doi.org/10.2320/matertrans.45.419

詳細

抄録

Fatigue tests were carried out on welded joints of commercial AZ31 alloy and AZ61 alloy in air as welded surface condition. Alloys were extruded or rolled to a plate shape. Pairs of the same type of alloy plates were butt-welded by tungsten inert gas (TIG) welding or friction stir welding (FSW). All welded joints except FSW-ed AZ61 have joint efficiency of around 90% for static tensile strength. Extruded AZ31 alloy joints by TIG or FSW showed fatigue joint efficiency of about 80%. However, fatigue joint efficiencies for other joints were at around 60%. Fracture surfaces showed brittle fatigue crack propagation; moreover, the directions of crack propagation were influenced remarkably by the microstructures.

責任著者(Corresponding author)

J-STAGEへの登録はこちら（無料）