2007 Volume 48 Issue 3 Pages 632-634
This letter presents microwave sintering of Ni52.5Zr15Nb10Ti15Pt7.5 glassy alloy powder. It was observed that the alloy was heated well in the magnetic field maximum, while it was not heated enough in the electric field maximum. A sintered sample with a glassy structure was obtained at 843 K in an inert atmosphere (Ar).